Product Name / Description Specification Packaging
Forged Grinding Ball 40mm - 125mm ø Diameter C: 0.6% - 1.00% | Si: 0.17% - 0.37% | Mn: 0.6% - 1.2% | P&S: ≤0.035% | Cr: 0.4% - 0.9% 850kg drums
1,000kg bags
2,000kg bags
Low Chromium - Cast Grinding Ball - 40mm - 125mm ø Diameter C: 2.1% - 3.60% | Si: ≤ 1.5% | Mn: ≤ 1.0% | P&S: ≤0.10% | Cr: 1%-2% 850kg drums
1,000kg bags
2,000kg bags
High Chromium - Cast Grinding Ball - 40mm - 100mm ø Diameter C: 2.0% - 3.30% | Si: ≤ 1.2% | Mn: ≤ 1.0% | P&S: ≤0.06% | Cr: 11% 850kg drums
1,000kg bags
2,000kg bags
Ceramic Beads CB 502 - 2.0 to 7.0mm ZrO₂ - 20% : SiO₂ - 35% : Al₂O₃ - 40% : Other 5% | Specific Density as gram /cm3 > 3.2 | Bulk Density as gram / cm³ - 2.05 - 2.25 | Moh's Hardness - 8 25kg bags
1,000kg bags
Yttrium Stabilized Ceramic Beads CB 505 - 2.0 to 7.0mm ZrO₂ - 94.6% : Y₂O₃ - 5.2 % : Other 0.2% |Specific Density as gram /cm3 > 6.0 | Bulk Density as gram / cm³ - > 3.7 | Moh's Hardness - 9 25kg bags
1,000kg bags
ZTA W Ceramic Beads CB 522 2.0 to 7.0mm ZrO₂ + Hfo₂ - 2% : SiO₂ - 4% : Al₂O₃ - 90% : Other 4% |Specific Density as gram /cm3 > 3.65 | Bulk Density as gram / cm³ - 2.3 | Moh's Hardness - 9 25kg bags
1,000kg bags
Oversized Ceramic Beads 25-75mm - Available in ZTA W composition. ZrO₂ + Hfo₂ - 2% : SiO₂ - 4% : Al₂O₃ - 90% : Other 4% | Specific Density as gram /cm3 > 3.65 | Bulk Density as gram / cm³ - 2.3 | Moh's Hardness - 9 25kg bags
1,000kg bags